XLPE AEI CT09-38:CT06-81A UK AEI Compounds
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| HalogenAcidGasEvolution | IEC 60754-1 | <0.50 % |
| Mechanical properties | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| tensile strength | IEC 60811-1-1 | 10.0 MPa | |
| Tensile strain | 断裂 | IEC 60811-1-1 | 140 % |
| flammability | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 33 % |
| aging | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| Change rate of tensile strength in air | 100°C,72hr,在IRM902油中 | -30 % | |
| Tensile stress change rate | 100°C,72hr,在IRM902油中，断裂 | -24 % | |
| Change rate of tensile strength in air | 120°C,168hr | IEC 60811-1-2 | 25 % |
| Tensile stress change rate | 100°C,24hr,在IRM902油中，断裂 | -25 % | |
| Change rate of tensile strength in air | 100°C,24hr,在IRM902油中 | -26 % | |
| Tensile stress change rate | 120°C,168hr，断裂 | IEC 60811-1-2 | -10 % |
| physical property | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | 内部方法 | 1.5 g/10min |
| density | BS2782620A | 1.51 g/cm³ |
| Thermal performance | Test Condition | Test Method | UK AEI Compounds/AEI CT09-38:CT06-81A |
|---|---|---|---|
| thermosetting | Elongationunderload,20N/cm²:200°C | IEC 60811-2-1 | 60 % |
| Permanentelongationaftercooling | IEC 60811-2-1 | 5.0 % |