PA66 FR350J NT0727 NA ASCEND USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASCEND USA/FR350J NT0727 NA |
|---|---|---|---|
| Tensile modulus | 23℃ | ISO 527 | 3200 Mpa |
| bending strength | ISO 178 | 90 Mpa | |
| Flexural modulus | 23℃ | ISO 178 | 3200 Mpa |
| elongation at break | 23℃ | ISO 527 | 15 % |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.3 kJ/m² |
| Simply supported beam without notch impact at 23 ℃ | ISO 179 | 65 kJ/m² | |
| tensile strength | 断裂,23℃ | ISO 527 | 70 Mpa |
| Poisson's ratio | ISO 527 | 0.4 | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 4.1 kJ/m² |
| Electrical performance | Test Condition | Test Method | ASCEND USA/FR350J NT0727 NA |
|---|---|---|---|
| Volume resistance 0.75mm | IEC 60093 | 1000000000000000000 Ω.㎝ | |
| dielectric strength | 1.0mm | IEC 60243 | 17 KV/mm |
| CTI 3.0mm | IEC 60112 | 250〜399 V |
| physical property | Test Condition | Test Method | ASCEND USA/FR350J NT0727 NA |
|---|---|---|---|
| Shrinkage rate | 流动，2.0mm，23℃ | ISO 294 | 1.4 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.9 % |
| 23℃ 24hr | ISO 62 | 0.8 % | |
| Shrinkage rate | 垂直，2.0mm，23℃ | ISO 294 | 1.7 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/FR350J NT0727 NA |
|---|---|---|---|
| Peak unannealed "MPa | ISO 75 | 75 °C | |
| Network melting temperature | ISO 11357 | 265 °C |