PPO
PPO SABIC INNOVATIVE US PPX7200U-BK1A363
Injection grade
US$ 4,900 / MT
FOB Guangzhou port, China
injectionTest ConditionTest MethodSABIC INNOVATIVE US/PPX7200U-BK1A363
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder250 to 290 °C
Spray nozzle temperature260 to 290 °C
Screw speed20 to 100 rpm
Mold temperature30 to 50 °C
Exhaust hole depth0.038 to 0.051 mm
Processing (melt) temperature260 to 290 °C
drying temperature60 to 65 °C
Suggested injection volume30 to 70 %
Temperature in the middle of the barrel240 to 280 °C
drying time2.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Temperature at the rear of the barrel225 to 275 °C
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/PPX7200U-BK1A363
Vicat softening temperature--ISO 306/B50103 °C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8311.1E-4 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64871.0 °C
Vicat softening temperature--ISO 306/B120107 °C
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648110 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8319.9E-5 cm/cm/°C
Vicat softening temperature--ASTM D152510146 °C
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/PPX7200U-BK1A363
Charpy Notched Impact Strength-30°CISO 179/1eA6.0 kJ/m²
Suspended wall beam without notch impact strength-30°C9ISO 180/1U无断裂
23°C9ISO 180/1U无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CASTM D48121400 J/m
Impact strength of simply supported beam without notch-30°CISO 179/1eU80 kJ/m²
Dart impact23°C, Total EnergyASTM D376336.0 J
Charpy Notched Impact Strength23°CISO 179/1eA12 kJ/m²
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/PPX7200U-BK1A363
elongationYield4ASTM D63810 %
YieldISO 527-2/508.2 %
Bending modulus50.0 mm Span5ASTM D7901440 Mpa
elongationBreak4ASTM D638130 %
bending strengthYield, 50.0 mm Span5ASTM D79048.0 Mpa
tensile strengthBreakISO 527-2/5028.0 Mpa
bending strength--6,7ISO 17848.0 Mpa
tensile strengthYield4ASTM D63833.0 Mpa
YieldISO 527-2/5034.0 Mpa
Tensile modulus--3ASTM D6381240 Mpa
--ISO 527-2/11670 Mpa
Bending modulus--6ISO 1781600 Mpa
tensile strengthBreak4ASTM D63827.0 Mpa
elongationBreakISO 527-2/50120 %
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/PPX7200U-BK1A363
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.60 - 0.80 %
Flow 2Internal Method0.060 - 0.080 %
Melt Volume Flow Rate (MVR)260°C/5.0 kgISO 113318.0 cm3/10min
melt mass-flow rate260°C/5.0 kgASTM D123816 g/10 min
Shrinkage rateFlow : 3.20 mmInternal Method0.60 - 0.80 %

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China