Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 241R SABIC INNOVATIVE US
LEXAN™
--
Low viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 800 J/m |
| 23°C | ASTM D4812 | 3200 J/m | |
| ASTM D1822 | 578 kJ/m² | ||
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 63.8 J |
| 23°C | ASTM D3029 | 169 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 130 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.5 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| tensile strength | 断裂 | ASTM D638 | 68.9 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| tensile strength | 屈服 | ASTM D638 | 62.1 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Dissipation Factor | 60Hz | ASTM D150 | 9E-04 |
| dielectric constant | 60Hz | ASTM D150 | 3.17 |
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.010 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| dielectric constant | 1MHz | ASTM D150 | 2.96 |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| UL flame retardant rating | 1.1mm | UL 94 | V-2 |
| 6.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| Outdoor applicability | UL 746C | f2 | |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.35 % |
| density | ASTM D792 | 1.19 g/cm³ | |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| Water absorption rate | 平衡,100°C | ASTM D570 | 0.58 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/241R |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 132 °C |
| thermal conductivity | ASTMC177 | 0.27 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| vicat | ASTM D15255 | 154 °C | |
| RTI Imp | UL 746 | 130 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| RTI Str | UL 746 | 130 °C | |
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| RTI Elec | UL 746 | 130 °C |