Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET 545-BK504K DUPONT JAPAN
Rynite®
Fiber grade
enhance、Glass fiber reinforced、High temperature resistan、Short fiber reinforcement、Filler: Glass fiber reinf、45% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | DUPONT JAPAN/545-BK504K |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Flexural modulus | ISO 178 | 14000 Mpa | |
| 23°C | ISO 178 | 14000 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 15500 Mpa |
| elongation at break | 23°C | ISO 527-2 | 1.9 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| Tensile modulus | ISO 527-1 | 15500 Mpa | |
| tensile strength | 23°C | ISO 527-2 | 175 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT JAPAN/545-BK504K |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 42 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+13 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | DUPONT JAPAN/545-BK504K |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 0.75mm |
| physical property | Test Condition | Test Method | DUPONT JAPAN/545-BK504K |
|---|---|---|---|
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.20 % |
| TD2.0mm | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | DUPONT JAPAN/545-BK504K |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 230 °C |
| vicat | 熔融温度 | ISO 11357-3 | 249 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 8.5E-05 cm/cm/°C | |
| UL flame retardant rating | UL 94 | HB |