PP PP GFM 25/15 natural (2118) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 42 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| hardness | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 100 MPa |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 40 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| dielectric strength | 3.00mm | IEC 60243-1 | 18 kV/mm |
| Volume resistivity | IEC 60093 | >2.0E+11 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| Flexural modulus | ISO 178 | 6600 MPa | |
| Fracture bending strain | ISO 178 | 3.6 % | |
| Tensile strain | 断裂 | ISO 527-2/50 | 3.5 % |
| Tensile modulus | ISO 527-2/1 | 6500 MPa | |
| bending strength | ISO 178 | 105 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 75.0 MPa |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.21 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.20 % | |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 13.5 cm³/10min |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ PP GFM 25/15 natural (2118) |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 163 °C |
| melting temperature | DIN EN11357-1 | 167 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 150 °C |