PA6 TS250G8F3A Black 浙江新力
--
高模量,尺寸稳定,热稳定,抗黄变
电热水壶温控器
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS250G8F3A Black |
|---|---|---|---|
| Tensile strength at break | IS0527 | 100 Mpa | |
| Yield bending strength | IS0178 | 155 Mpa | |
| Flexural modulus | IS0178 | 8000 Mpa | |
| elongation at break | IS0527 | 2.0 % | |
| Charpy Notched Impact Strength | 3.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | 28 kJ/m² |
| other | Test Condition | Test Method | 浙江新力/TS250G8F3A Black |
|---|---|---|---|
| Linear forming shrinkage rate | IS02577 | 0.6 % | |
| proof tracking index | IEC60112 | 250 3mm/v | |
| Surface Resistivity | IEC60093 | 1.00E+13 Q |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS250G8F3A Black |
|---|---|---|---|
| Flame retardant performance UL94 | 厚度2.0mm | UL94 | V-2 ℃ |
| 厚度0.8mm | UL94 | ℃ | |
| 厚度1.5mm | UL94 | ℃ | |
| 厚度3.0mm | UL94 | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS250G8F3A Black |
|---|---|---|---|
| density | 1.55 g/cm³ | ||
| Water absorption rate | IS062 | 1.0 % |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS250G8F3A Black |
|---|---|---|---|
| GWIT | 厚度3.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度3.0mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度1.5mm | IEC60695-2-13 | ℃ |
| 厚度0.8mm | IEC60695-2-13 | ℃ | |
| Heat distortion temperature | 1.8MPa | IS076 | 185 ℃ |
| 0.45MPa | IS076 | ℃ | |
| GWFI | 厚度0.8mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度2.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度2.0mm | IEC60695-2-12 | ℃ |
| 厚度1.5mm | IEC60695-2-12 | 960 ℃ |