PA6 B1X25 HI Repol Engineering Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Repol Engineering Plastics/B1X25 HI |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 1900 MPa |
| Tensile strain | 屈服 | ISO 527-2/5 | 4.0 % |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 75.0 kJ/m² |
| 简支梁无缺口冲击强度 | ISO 179/1eU | NB | |
| Flexural modulus | ISO 178 | 1400 MPa | |
| bending strength | ISO 178 | 60.0 MPa | |
| Flexural modulus | 23°C | ISO 178 | 1300 MPa |
| tensile strength | 断裂 | ISO 527-2/5 | 50.0 MPa |
| elongation at break | 屈服，23°C | ISO 527-2 | 130 % |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| tensile strength | 23°C | ISO 527-2 | 50.0 MPa |
| elongation at break | 23°C | ISO 527-2 | 4.0 % |
| Tensile modulus | ISO 527-2/1 | 1900 MPa | |
| bending strength | 23°C | ISO 178 | 55.0 MPa |
| physical property | Test Condition | Test Method | Repol Engineering Plastics/B1X25 HI |
|---|---|---|---|
| Water absorption rate | ISO 15512/A | <=0.25 % | |
| density | ISO 1183 | 1.07 g/cm³ |
| Thermal performance | Test Condition | Test Method | Repol Engineering Plastics/B1X25 HI |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 50.0 °C |
| vicat | ISO 306 | > 200 °C | |
| 50N | ISO 306/A50 | >=200 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 50.0 °C |