PA46 TS35O(BK) DSM HOLAND

Stanyl®

Electronic and electrical components,Casters

Flame retardant

UL

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	280 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	190 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion		Flow	ISO 11359-2	8.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	295 °C

mechanical properties	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
Bending modulus	--	ISO 178	3000 Mpa
		120°C	ISO 178	800 Mpa
		160°C	ISO 178	600 Mpa
Nominal tensile fracture strain	160°C	ISO 527-2	> 50 %
		180°C	ISO 527-2	> 50 %
		120°C	ISO 527-2	> 50 %
		--	ISO 527-2	40 %
		200°C	ISO 527-2	> 50 %
Tensile modulus	200°C	ISO 527-2	500 Mpa
		--	ISO 527-2	3300 Mpa
		120°C	ISO 527-2	800 Mpa
		160°C	ISO 527-2	650 Mpa
		180°C	ISO 527-2	600 Mpa
tensile strength	Yield, 120°C	ISO 527-2	50.0 Mpa
		Yield, 160°C	ISO 527-2	40.0 Mpa
		Yield, 200°C	ISO 527-2	30.0 Mpa
		Yield, 180°C	ISO 527-2	35.0 Mpa
		Yield	ISO 527-2	100 Mpa

Electrical performance	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
Dielectric strength		IEC 60243-1	25 KV/mm
Relative permittivity	100 Hz	IEC 60250	4.00
Relative permittivity		1 MHz	IEC 60250	3.60
Volume resistivity		IEC 60093	1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
density		ISO 1183	1.18 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	2.0 %
Shrinkage rate		Flow	ISO 294-4	2.0 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.7 %

impact performance	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	10 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	无断裂

flammability	Test Condition	Test Method	DSM HOLAND/TS35O(BK)
Flammability level		UL 94	V-2