Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PTS PCA-2201NHV PTS USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTM D256 | 590 J/m |
| Electrical performance | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| Hot wire ignition (HWI) | 3.00mm | UL 746 | PLC 1 sec |
| High arc combustion index (HAI) | 2.50mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.50mm | UL 746 | PLC 2 sec |
| 1.5mm | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 2.50mm | UL 746 | PLC 2 sec |
| High arc combustion index (HAI) | 3.00mm | UL 746 | PLC 0 |
| 2.5mm | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 mm/min |
| dielectric strength | ASTM D149 | 18 kV/mm | |
| Hot wire ignition (HWI) | 2.5mm | UL 746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 1.50mm | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| Flexural modulus | 3.17mm | ASTM D790 | 2690 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 60.0 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 88.9 MPa |
| elongation | 断裂,3.17mm | ASTM D638 | 65 % |
| flammability | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 950 °C |
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 925 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 700 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 925 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 12 g/10min |
| density | ASTM D792 | 1.17 g/cm³ |
| Thermal performance | Test Condition | Test Method | PTS USA/PTS PCA-2201NHV |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |