PC H-3000VR MITSUBISHI THAILAND
IUPILON™
parts、Fitness equipment
High mobility、Flame retardant、Demolding ability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI THAILAND/H-3000VR |
|---|---|---|---|
| Stretching length | ASTM D638 | 90-140 % | |
| Flexural modulus | ASTM D790 | 2.3 GPa | |
| bending strength | ASTM D790 | 80.4-90.2 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 98 J/m | |
| tensile strength | ASTM D638 | 58.8-68.6 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI THAILAND/H-3000VR |
|---|---|---|---|
| Dielectric loss | 10，正切 | ASTM D150 | 0.0082 |
| dielectric constant | 10 | ASTM D150 | 25.2 Pf/m |
| dielectric strength | ASTM D149 | 18-22 KV/mm |
| physical property | Test Condition | Test Method | MITSUBISHI THAILAND/H-3000VR |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 05-0.8 % | |
| Water absorption rate | 23℃,24hrs | ASTM D570 | 0.23-0.26 % |
| Rockwell hardness | ASTM D785 | 123 R | |
| Shrinkage rate | 垂直方向 | 05-0.8 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI THAILAND/H-3000VR |
|---|---|---|---|
| Heat distortion temperature | 18.6kgf/cm，HDT | ASTM D648 | 125-130 °C |
| combustibility | UL 94 | V-2 | |
| Heat distortion temperature | 4.6kgf/cm，HDT | ASTM D648 | 130-135 °C |
| Linear coefficient of thermal expansion | 6-7 |