PC EXL1130T SABIC INNOVATIVE US
LEXAN™ 
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
RTIElecUL746130 °C
Ball PressureTest125°CIEC60695-10-2Pass
Heat Deflection Temperature1.8MPa,未退火,3.20mmASTMD648124 °C
RTIStrUL746125 °C
Vicat Softening Temperature--ISO306/B120146 °C
Linear thermal expansion coefficientMD：23到80°CISO11359-27.2E-05 cm/cm/°C
MD：-40到40°CASTME8317E-05 cm/cm/°C
Heat Deflection Temperature1.8MPa,Unannealed,100mmSpanISO75-2/Ae128 °C
Vicat Softening Temperature--ISO306/B50145 °C
Heat Deflection Temperature0.45MPa,未退火,3.20mmASTMD648139 °C
Linear thermal expansion coefficientTD：-40到40°CASTME8317.5E-05 cm/cm/°C
Heat Deflection Temperature0.45MPa,Unannealed,100mmSpanISO75-2/Be140 °C
Vicat Softening TemperatureASTMD152510145 °C
Evolution Calendar intelligent importerUL746120 °C
Linear thermal expansion coefficientTD：23to80°CISO11359-27.2E-05 cm/cm/°C
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Rockwell HardnessL计秤ASTMD78589
R计秤ASTMD785121
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Moisture Absorption平衡,23°C,50%RHISO620.15 %
Modeling ShrinkageMD：3.20mm内部方法0.40to0.80 %
Melt Mass-Flow Rate300°C/1.2kgASTMD123810 g/10min
Modeling ShrinkageTD：3.20mm内部方法0.40to0.80 %
Melt Volume flow Rate300°C/1.2kgISO11339.00 cm3/10min
Moisture Absorption饱和,23°CISO620.35 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Flexural Modulus50.0mm跨距ASTMD7902230 Mpa
Tensile Stress断裂ISO527-2/5060.0 Mpa
Tensile Elongation断裂ASTMD63898 %
Tensile Strain断裂ISO527-2/50120 %
Tensile ModulusISO527-2/12150 Mpa
Tensile Strength屈服ASTMD63855.5 Mpa
Flexural ModulusISO1782250 Mpa
Flexural Strength屈服,50.0mm跨距ASTMD79092.4 Mpa
Tensile Elongation屈服ASTMD6386.0 %
Tensile Stress屈服ISO527-2/5057.0 Mpa
Tensile Strain屈服ISO527-2/506.0 %
Flexural StrengthISO17885.0 Mpa
Tensile ModulusASTMD6382020 Mpa
Tensile Strength断裂ASTMD63850.3 Mpa
OtherTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
purposeIT办公
characteristic高流动 耐寒
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Notched Izod Impact Strength-30°CISO180/1A60 kJ/m²
Charpy Unnotched Impact Strength-30°CISO179/1eUNoBreak
Unnotched Izod Impact Strength-30°CISO180/1UNoBreak
Charpy Notched Impact Strength-30°CISO179/1eA65 kJ/m²
Instrumented Dart Impact23°C,TotalEnergyASTMD376370.0 J
Charpy Notched Impact Strength23°CISO179/1eA70 kJ/m²
Charpy Unnotched Impact Strength23°CISO179/1eUNoBreak
Unnotched Izod Impact Strength23°CISO180/1UNoBreak
Notched Izod Impact Strength23°CISO180/1A70 kJ/m²
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Glow Wire Ignition Temperature1.0mmIEC60695-2-13875 °C
3.0mmIEC60695-2-13875 °C
Glow Wire Flammability Index0.8mmIEC60695-2-12850 °C
Oxygen IndexISO4589-237 %
Glow Wire Flammability Index1.0mmIEC60695-2-12960 °C
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1130T
Surface ResistivityASTMD257>1.0E+15 ohms
Volume ResistivityASTMD257>1.0E+15 ohms·cm
Dielectric Constant100HzASTMD1502.68
Dissipation Factor?1MHzASTMD1509.3E-03
100HzASTMD1501.2E-03
Dielectric Constant1MHzASTMD1502.64
Dielectric Strength0.800mm,inOilASTMD14916 KV/mm