Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PX1112-701 SABIC INNOVATIVE US
NORYL™
Automotive body panels、Automotive sector
Dimensional stability、Low Specific Gravity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE US/PX1112-701
Melt Volume-Flow Rate (MVR)
280°C/5.0 kg
ISO 1133
cm3/10min
6
Shrinkage rate - Flow
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE US/PX1112-701
Impact strength of simply supported beam gap
-30°C
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap
23°C
ISO 179/1eA
kJ/m²
1
Tensile modulus
ISO 527-2/1
Mpa
2
tensile strength
屈服
ISO 527-2/50
Mpa
4
tensile strength
断裂
ISO 527-2/50
Mpa
4
Ball pressure hardness
H 358/30
ISO 2039-1
Mpa
8
elongation
屈服
ISO 527-2/50
%
3
elongation
断裂
ISO 527-2/50
%
3
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
内部方法
mg
6
Bending modulus
ISO 178
Mpa
1
Bending stress 2,
ISO 178
Mpa
7
Suspended wall beam gap impact strength
-30°C
ISO 180/1A
kJ/m²
1
Suspended wall beam gap impact strength
23°C
ISO 180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE US/PX1112-701
thermal conductivity
ISO 8302
W/m/K
0
Hot deformation temperature
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距
ISO 75-2/Be
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距
ISO 75-2/Ae
°C
1
vicat softening point
--
ISO 306/A50
°C
1
vicat softening point
--
ISO 306/B50
°C
1
vicat softening point
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE US/PX1112-701
Surface resistivity
IEC 60093
ohms
>
Volume resistivity
IEC 60093
ohms·cm
1