PBT HR5330HF-NC010 DUPONT USA
Cristin®
Electronic and electrical
Hydrolysis resistance、Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5330HF-NC010
density
ISO 1183
g/cm
1
density
ISO1183
g/cm³
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
0
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
0
Stickiness number
ISO307
cm³/g
9
Mechanical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5330HF-NC010
Charpy non notched impact strength
23 ℃, Type 1, Edgewise
ISO 179
KJ/m
Impact strength of simply supported beam gap
-，-30 ℃, Type 1, Edgewise, Notch A
ISO 179
KJ/m
1
Impact strength of simply supported beam gap
-，23 ℃, Type 1, Edgewise, Notch A
ISO 179
KJ/m
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
7
Tensile modulus
23℃
ISO 527-1, -2
Mpa
8
Tensile modulus
ISO527-2
Mpa
8
tensile strength
断裂
ISO527-2
Mpa
1
Yield point tensile strain
23℃
ISO 527-1, -2
%
Yield point tensile stress
23℃
ISO 527-1, -2
Mpa
1
Gap impact strength
-，-40 ℃, Type 1, Notch A
ISO 180
KJ/m
Gap impact strength
-，23 ℃, Type 1, Notch A
ISO 180
KJ/m
elongation
断裂
ISO527-2
%
3
Bending modulus
ISO178
Mpa
7
Bending modulus
23℃
ISO 178
Mpa
bending strength
23℃
ISO 178
Mpa
bending strength
ISO178
Mpa
2
Impact strength of cantilever beam gap
-40°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Cantilever beam without notch impact strength
23°C
ISO180/1U
kJ/m²
6
Thermal performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5330HF-NC010
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
ISO 3146
℃
2
Melting temperature
ISO11357-3
°C
2
vicat softening point
ISO306/B50
°C
2
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：55to160°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5330HF-NC010
Surface resistivity
IEC60093
ohms
1
Dielectric strength
--
IEC60243-1
KV/mm
4
Dielectric strength
1.00mm5
IEC60243-1
KV/mm
3
Leakage Trace Index
IEC60112
V
4
Volume resistivity
IEC60093
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PBT/DUPONT USA/HR5330HF-NC010
Extreme Oxygen Index
ISO4589-2
%
1
Burning rate
1.00mm
ISO3795
mm/min
3