Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM1014-V0 TORAY JAPAN
Amilan®
electrical equipment
Low halogen content
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 120 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | 5.20 -- | |
| arc resistance | sec | 120 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | -- |
| Dissipation Factor | 23°C,1MHz | 0.080 -- | |
| Volume resistivity | ohms·cm | 1E+15 -- | |
| dielectric strength | kV/mm | 30 -- |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| tensile strength | 23°C | MPa | 80.0 45.0 |
| Taber abraser | 1000Cycles | mg | 5.00to6.00 -- |
| Tensile strain | 断裂,23°C | % | 7.5 37 |
| Flexural modulus | 80°C | MPa | 1000 -- |
| bending strength | -40°C | MPa | 150 -- |
| 80°C | MPa | 55.0 -- | |
| Tensile strain | 断裂,80°C | % | 56 -- |
| Flexural modulus | 23°C | MPa | 3500 1200 |
| tensile strength | 80°C | MPa | 40.0 -- |
| bending strength | 23°C | MPa | 115 45.0 |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| UL flame retardant rating | 0.79mm | V-0 -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 9.5 -- |
| Shrinkage rate | MD：1.00mm3 | % | 0.40-0.80 -- |
| MD：3.00mm4 | % | 1.0-1.3 -- | |
| Water absorption rate | 23°C,24hr | % | 1.7 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1014-V0 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 207 -- |
| melting temperature | °C | 225 -- |
Contact Us