Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CY4000 7M1D100 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electronic and electrical、Shell
high strength、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039 | 110 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| Tensile modulus | 23℃ | ISO 527 | 2700 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 2500 Mpa |
| vicat | 50℃/hr 50N | ISO 306 | 85 °C |
| Taber wear resistance | 1kg | 15 mg/1000cy | |
| elongation | 23℃ | ISO 527 | 40 % |
| Heat distortion temperature | 未退火1.8MPa，HDT | ISO 75 | 72 °C |
| elongation | 屈服23℃ 50mm/min | ISO 527 | 3 % |
| tensile strength | 屈服23℃ | ISO 527 | 55 Mpa |
| Linear coefficient of thermal expansion | 垂直 | ISO 11359 | 0.000080 cm/cm/℃ |
| vicat | 120℃/hr 50N | ISO 306 | 90 °C |
| bending strength | 屈服23℃ | ISO 178 | 85 Mpa |
| Impact strength of cantilever beam gap | -30℃ | ISO 180 | 10 kJ/m² |
| Heat distortion temperature | 未退火0.45MPa，HDT | ISO 75 | 85 °C |
| Charpy Notched Impact Strength | -30℃ | ISO 179 | 10 kJ/m² |
| 23℃ | ISO 179 | 10 kJ/m² | |
| tensile strength | 23℃ 50mm/min | ISO 527 | 45 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 10 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 0.006 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1000000000000000 Ω.cm | |
| dielectric strength | 3.2mm | IEC 60243 | 17 KV/mm |
| dielectric constant | IEC 60250 | 2.7 | |
| 1MHz | IEC 60250 | 2.7 | |
| Dispersion factor 1MHz | IEC 60250 | 0.006 | |
| Surface Resistivity | IEC 60093 | 1000000000000000 |
| UL | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| RTI Str | 3.0mm | UL 746B | 60 °C |
| RTI Elec | 3.0mm | UL 746B | 60 °C |
| RTI Str | 2.5mm | UL 746B | 60 °C |
| RTI Imp | 3.0mm | UL 746B | 60 °C |
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| RTI Elec | 2.5mm | UL 746B | 60 °C |
| RTI Imp | 2.5mm | UL 746B | 60 °C |
| Flame retardant performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589 | 29 % | |
| Relative temperature of heating wire | 3.2mm | IEC 60695 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY4000 7M1D100 |
|---|---|---|---|
| melt mass-flow rate | 260℃ 2.16kg | ISO 1133 | 21 g/10min |
| Shrinkage rate | 流动 | ISO 294 | 0.4 % |
| ISO 294 | 0.6 % | ||
| melt mass-flow rate | 260℃ 2.16kg | ASTM D1238 | 23 g/10min |
| density | ISO 1183 | 1.2 g/cm³ |