POK M330F HYOSUNG KOREA
POKETONE™
automobile、Electronic appliances、Industrial materials
High mobility、High impact resistance、High chemical resistance、High wear resistance、High gas barrier、High flame retardancy
TDS
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | HYOSUNG KOREA/M330F |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30℃ | ISO 180/1A | 3 kJ/m² |
| -10℃ | ISO 180/1A | 4 kJ/m² | |
| Suspended wall beam without notch impact strength | ASTM D256 | N.B. | |
| Impact strength of cantilever beam gap | -10℃ | ASTM D256 | 60 kJ/m² |
| 23℃ | ASTM D256 | 95 kJ/m² | |
| 23℃ | ISO 180/1A | 7 kJ/m² | |
| -30℃ | ASTM D256 | 40 kJ/m² | |
| Dart impact | 23℃ | ISO 6603-2 | 50 J |
| Mechanical properties | Test Condition | Test Method | HYOSUNG KOREA/M330F |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1600 Mpa | |
| elongation at yield | ASTM D638 | 21 % | |
| Flexural modulus | ASTM D790 | 1500 | |
| bending strength | ASTM D790 | 57 Mpa | |
| Flexural modulus | ISO 178 | 1400 | |
| tensile strength | 屈服 | ASTM D638 | 60 Mpa |
| elongation at break | ASTM D638 | 300 % | |
| Tensile modulus | ISO 527-1 | 1500 Mpa |
| Electrical performance | Test Condition | Test Method | HYOSUNG KOREA/M330F |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1000000000000000000 ohm/sq | |
| dielectric constant | 60Hz | IEC 250 | 5 |
| Dissipation Factor | 60Hz | ASTM D150 | 0.008 |
| Compared to the Leakage Tracking Index (CTI) | IEC 112 | V | |
| dielectric constant | 60Hz | ASTM D150 | 6.2 |
| Dissipation Factor | 60Hz | IEC 250 | 0.013 |
| Volume resistivity | ASTM D257 | 1000000000000000 ohms·cm | |
| dielectric strength | 短期，3 mm | ASTM D149 | 15 KV/mm |
| 短期，2 mm | ASTM D149 | 19 KV/mm | |
| arc resistance | ASTM D495 | 130 sec |
| physical property | Test Condition | Test Method | HYOSUNG KOREA/M330F |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 110 | |
| Shrinkage rate | TD, 2 mm | ASTM D955 | 1.5 % |
| TD, 3 mm | ASTM D955 | 2 % | |
| MD, 2 mm | ASTM D955 | 1.6 % | |
| Shore hardness | ISO 868 | 77 | |
| melt mass-flow rate | 240℃，2.16kg | ISO 1133 | 56 |
| saturation | ASTM D570 | 2.1 % | |
| Water absorption rate | 平衡，50%RH | ASTM D570 | 0.5 % |
| melt mass-flow rate | 240℃，2.16kg | ASTM D1238 | 60 g/10min |
| Shrinkage rate | MD, 3 mm | ASTM D955 | 2 % |
| Thermal performance | Test Condition | Test Method | HYOSUNG KOREA/M330F |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa，HDT | ISO 75 | 190 °C |
| 1.8 MPa，HDT | ISO 75 | 92 °C | |
| melting temperature | ASTM D955 | 222 °C | |
| Heat distortion temperature | 264psi，HDT | ASTM D648 | 105 °C |
| vicat | 5 kg | ASTM D-1525 | 195 °C |
| Linear coefficient of thermal expansion | 25℃ to 55℃ | ASTM E831 | 0.000097 |
| Heat distortion temperature | 66psi，HDT | ASTM D648 | 200 °C |
| vicat | 50 N | ISO 306/B50 | 190 °C |