LCP E481i BK210P TAIWAN POLYPLASTICS
LAPEROS®
Automotive components,Laptop case,Electronic and Electrical Applications,Home appliance applications
Low anisotropy,Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Rockwell hardness | M -Sale | ISO 2039-2 | 60 |
thermal performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 260 °C |
mechanical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Bending modulus | ISO 178 | 13000 Mpa | |
Bending strain | ISO 178 | 1.7 % | |
bending strength | ISO 178 | 160 Mpa | |
elongation | Break | ASTM D638 | 1.6 % |
tensile strength | ASTM D638 | 115 Mpa |
Electrical performance | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Arc resistance | ASTM D495 | 182 sec | |
Compared to the anti leakage trace index | IEC 60112 | V | |
Dielectric strength | 1.00 mm | IEC 60243-1 | 47 KV/mm |
3.00 mm | IEC 60243-1 | 25 KV/mm | |
Dissipation factor | 1 kHz | IEC 60250 | 0.020 |
1 MHz | IEC 60250 | 0.020 | |
Relative permittivity | 1 MHz | IEC 60250 | 4.10 |
1 kHz | IEC 60250 | 4.80 | |
Volume resistivity | IEC 60093 | 2.0E+16 ohms·cm |
Physical properties | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Shrinkage rate | Flow : 1.00 mm | Internal Method | 0.060 % |
横向Flow : 1.00 mm | Internal Method | 0.28 % | |
Water absorption rate | 24 hr, 23°C | ISO 62 | 0.020 % |
flammability | Test Condition | Test Method | TAIWAN POLYPLASTICS/E481i BK210P |
---|---|---|---|
Color number | VF2201/BK210P | ||
UL flame retardant rating | UL 94 | V-0 |