PBT BASF GERMANY B4300K6

Enhanced level

US$ 4,480 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	BASF GERMANY/B4300K6
Relative permittivity	1 MHz1 MHz	IEC 60250	3.8
Dissipation factor	1 MHz1 MHz	IEC 60250	0.019
Relative permittivity	100 Hz100 Hz	IEC 60250	3.8
Volume resistivity		IEC 60093	10000000000000000 ohms·cm
Surface resistivity		IEC 60093	10000000000000 ohms
Dissipation factor	100 Hz100 Hz	IEC 60250	0.0012
thermal performance	Test Condition	Test Method	BASF GERMANY/B4300K6
Maximum operating temperature	short cycle operation		200 °C
Temperature index - at 51% loss of tensile strength	---- 77	IEC 60216	130 °C
specific heat			1500 J/kg/℃
Hot deformation temperature	1.8 MPa，Unannealed264 psi, Unannealed	ISO 75-2/A	95 °C
Hot deformation temperature		0.45 MPa，Unannealed66 psi, Unannealed	ISO 75-2/B	200 °C
thermal conductivity		DIN 52612	0.27 W/m/K
Linear coefficient of thermal expansion	MD：23~80℃MD：23 to 80℃	ISO 11359-2	7.0E-5 - 8.0E-5 1/℃
Temperature index - at 50% loss of tensile strength	---- 66	IEC 60216	120 °C
Melting temperature		ISO 11357-3	223 °C
mechanical properties	Test Condition	Test Method	BASF GERMANY/B4300K6
Ball Pressure Test	H358/30	ISO 2039-1	165 Mpa
Tensile strain	BreakBreak	ISO 527-2	5 %
tensile strength	BreakBreak	ISO 527-2	50 Mpa
Tensile modulus		ISO 527-2	4000 Mpa
Tensile creep modulus	1000 hr1000 hr5	ISO 899-1	2200 Mpa
Physical properties	Test Condition	Test Method	BASF GERMANY/B4300K6
Melt Volume Flow Rate (MVR)	250℃，2.16 kg250℃/2.16 kg	ISO 1133	9 cm3/10min
Shrinkage rate	TD：自由的free, transverse		1.7 %
Shrinkage rate		MD：自由的free, longitudinal		1.7 %
Water absorption rate	Saturation，23℃Saturation, 73°F	ISO 62	0.4 %
Stickiness		ISO 307	113 cm³/g
Water absorption rate	Equilibrium，23℃，50% RHEquilibrium, 73°F, 50% RH	ISO 62	0.2 %
Apparent density			0.70 to 0.80 g/cm³
impact performance	Test Condition	Test Method	BASF GERMANY/B4300K6
Impact strength of simply supported beam without notch	-30°C -30°C	ISO 179/1eU	24 kJ/m²
Impact strength of simply supported beam without notch		23℃23°C	ISO 179/1eU	35 kJ/m²
flame retardant performance	Test Condition	Test Method	BASF GERMANY/B4300K6
UL flame retardant rating	1.6 mm		HB
UL flame retardant rating		0.75 mm		HB