Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 TS250G6F4A-LM Black 浙江新力
--
高耐热性,尺寸稳定性,高阻燃等级,可激光打标
塑壳断路器等电子电器外壳
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS250G6F4A-LM Black |
|---|---|---|---|
| Yield bending strength | ISO178 | 220 Mpa | |
| Tensile strength at break | ISO527 | 140 Mpa | |
| Flexural modulus | ISO178 | 10000 Mpa | |
| Charpy Notched Impact Strength | 15 kJ/m² | ||
| Impact strength of simply supported beam without notch | 60 kJ/m² | ||
| elongation at break | ISO527 | 2.2 % |
| other | Test Condition | Test Method | 浙江新力/TS250G6F4A-LM Black |
|---|---|---|---|
| Linear forming shrinkage rate | ISO2577 | 0.6 % | |
| Surface Resistivity | IEC60093 | 1.00E+13 Ω | |
| proof tracking index | IEC60112 | 500 3mm/v |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS250G6F4A-LM Black |
|---|---|---|---|
| UL94 | 厚度1.5mm | ℃ | |
| 厚度0.8mm | ℃ | ||
| 厚度3.0mm | V0 ℃ | ||
| 厚度2.0mm | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS250G6F4A-LM Black |
|---|---|---|---|
| Water absorption rate | ISO62 | % | |
| density | 1.45 g/cm³ |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS250G6F4A-LM Black |
|---|---|---|---|
| GWIT | 厚度3.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度3.0mm | IEC60695-2-12 | 960 ℃ |
| GWIT | 厚度1.5mm | IEC60695-2-13 | ℃ |
| 厚度0.8mm | IEC60695-2-13 | ℃ | |
| GWFI | 厚度0.8mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度2.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度2.0mm | IEC60695-2-12 | ℃ |
| Hot deformation temperature 1.8MPa | ISO76 | 190 ℃ | |
| Hot deformation temperature 0.45MPa | ISO76 | ℃ | |
| GWFI | 厚度1.5mm | IEC60695-2-12 | ℃ |