HIPS HIPS-514 SECCO SHANGHAI
--
Toy、Electronic field、Electrical field
heat-resisting、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SECCO SHANGHAI/HIPS-514 |
|---|---|---|---|
| density | ISO 1183/1987 | 1030 kg/m | |
| melt mass-flow rate | 200℃/5Kg | ISO 1133/1997 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | SECCO SHANGHAI/HIPS-514 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/1993 | 23 Mpa |
| elongation | 50mm/min | ISO 527-2/1993 | 50 % |
| Impact strength of cantilever beam gap | ISO 180/1993 | 750 J/m | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 750 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| Flexural modulus | 2mm/min | ISO 178/1993 | 2000 Mpa |
| tensile strength | ASTM D638/ISO 527 | 23 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | SECCO SHANGHAI/HIPS-514 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.03 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | SECCO SHANGHAI/HIPS-514 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 74 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 85 ℃（℉） | |
| Heat distortion temperature | 1.82MPa，HDT | ISO 75-2/1993 | 74 °C |
| vicat | B50/oil | ISO 306/1994 | 85 °C |