Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS T80 901510 COVESTRO GERMANY
Bayblend®
engineering application ,Electronic and electrical accessories
High mobility,Non enhanced,Good appearance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | COVESTRO GERMANY/T80 901510 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 42 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2500 Mpa |
| elongation at break | 23°C | ISO 527-2 | >50 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 14 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 62 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO GERMANY/T80 901510 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 45 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+17 Ω.cm | |
| dielectric strength | 相对漏电起痕指数 | IEC 60112 | 175 V |
| Volume resistivity | IEC 60093 | 1E+16 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | COVESTRO GERMANY/T80 901510 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 0.85mm |
| physical property | Test Condition | Test Method | COVESTRO GERMANY/T80 901510 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.70 % |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.65 % |
| melt mass-flow rate | 260℃/5.0Kg | ISO 1133 | 27 cm3/10min |
| Water absorption rate | (23°C,50RH) | ISO 62 | 0.20 % |
| Shrinkage rate | TD2.0mm | ISO 294-4 | 0.65 % |
| Thermal performance | Test Condition | Test Method | COVESTRO GERMANY/T80 901510 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 108 °C |
| vicat | ISO 306/B50 | 128 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 127 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7.2E-05 cm/cm/°C |