Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

TPV 8211-65 CELANESE USA

Santoprene™

packing,Automotive sector,Soft handle,Smart phone,Consumer goods sector,Phone,Soft handle,Consumer product application field,packing,Application in the automotive field

dimensional stability ,Low friction coefficient,Recyclable materials,Cleanable,Good forming performance,Good colorability,High mobility,Ozone resistance,Chemical resistance,soft,Low water absorption,Not absorbing water

Plastic Datasheets

hardness	Test Condition	Test Method	CELANESE USA/8211-65
Shore hardness	ShoreA,15Sec,23°C	ISO 868	70

thermal performance	Test Condition	Test Method	CELANESE USA/8211-65
Brittle temperature		ISO 812	-63.0 °C
Brittle temperature			ASTM D746	-63.0 °C
RTI Elec		UL 746	100 °C
RTI Str	3.0mm	UL 746	95.0 °C
RTI Str		1.1mm	UL 746	90.0 °C

flammability	Test Condition	Test Method	CELANESE USA/8211-65
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating		1.1mm	UL 94	HB

elastomer	Test Condition	Test Method	CELANESE USA/8211-65
elongation	Break,23°C，Across Flow	ISO 37	510 %
elongation		Break,23°C，Across Flow	ASTM D412	510 %
Permanent compression deformation	125°C,70hr	ISO 815	55 %
		70°C,22hr	ISO 815	29 %
		70°C,22hr	ASTM D395B	29 %
		125°C,70hr	ASTM D395B	55 %
tensile strength	Break,23°C	ISO 37	5.50 Mpa
tensile strength		Break,23°C，横向Flow	ASTM D412	5.50 Mpa
Tensile stress	100%Strain,23°C，横向Flow	ASTM D412	2.50 Mpa
Tensile stress		100%Strain,23°C，横向Flow	ISO 37	2.50 Mpa

aging	Test Condition	Test Method	CELANESE USA/8211-65
Change rate of tensile strength in air	150°C,168hr	ASTM D573	-11 %
Change rate of tensile strength in air		150°C,168hr	ISO 188	-11 %
Change rate of ultimate elongation in air	150°C,168hr	ASTM D573	-18 %
Hardness change rate in the air	ShoreA,150°C,168hr	ASTM D573	-2.0
Shore hardness	ShoreA,150°C,168hr	ISO 188	-2.0