PBT 5174G-R TORAY JAPAN
Toraycon®
Electrical applications,Electrical components
Flame retardant,High impact resistance,Filler: Glass fiber reinf,20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 57 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 113 mm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Friction coefficient - vs. Metal | SuzukiMethod | 0.16 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.1 % |
| bending strength | 23°C | ISO 178 | 150 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 95.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 6300 Mpa |
| coefficient of friction | 0.20 | ||
| Tensile modulus | 23°C | ISO 527-2 | 6600 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.80 |
| 23°C,1kHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 |
| flammability | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.90 % |
| MD:3.00mm4 | 内部方法 | 0.40 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5174G-R |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 207 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 5E-05 cm/cm/°C |