Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET 545 NC010 DUPONT USA
Rynite®
Fiber grade
enhance、Glass fiber reinforced、High temperature resistan、Short fiber reinforcement
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 40 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| M计秤 | ISO 2039-2 | 100 |
| Electrical performance | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.00E+14 Ω | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 4.4 | |
| relative permittivity | 100Hz | IEC 60250 | 4.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| relative permittivity | 1MHz | IEC 60250 | 4.40 |
| Volume resistivity | ASTM D257/IEC 60093 | 1.00E+13 Ω.cm | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.011 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 15500 Mpa | |
| ASTM D412/ISO 527 | 15500 kg/cm²(MPa)[Lb/in²] | ||
| Tensile creep modulus | 1hr | ISO 899-1 | 15600 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 13500 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | ISO 178 | 13500 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 13300 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 182 Mpa |
| Rockwell hardness | ASTM D785 | 100 |
| other | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| characteristic | 45%矿物/玻纤增强.强度和刚度.尺寸稳定性和抗蠕变 |
| Physical properties | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.85 % | |
| density | ASTM D792/ISO 1183 | 1690 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.14 % |
| flammability | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| Fogging-G-value | condensate | ISO 6452 | 0.0 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 2.50 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.62 % |
| Ejection Temperature | 170 °C | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.14 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/545 NC010 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melting temperature | ISO 11357-3 | 252 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 226 ℃（℉） |
| Effective thermal diffusivity coefficient | 1.4E-07 m²/s | ||
| thermal conductivity | 0.32 W/m/K | ||
| vicat | ISO 306/B50 | 230 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 226 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.5E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 180 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 8.3E-05 cm/cm/°C |