Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 8231G HS BASF GERMANY
Ultramid®
Helmet、Automotive Applications、Engine parts
Thermal stability、high strength、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 40 kJ/m² |
| hardness | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| elongation | Break,121°C | ASTM D638 | 7.0 % |
| tensile strength | 断裂,-40°C | ISO 527-2 | 160 Mpa |
| 断裂,80°C | ISO 527-2 | 60.0 Mpa | |
| Tensile modulus | 80°C | ISO 527-2 | 2470 Mpa |
| Flexural modulus | -40°C | ASTM D790 | 5860 Mpa |
| bending strength | 23°C | ASTM D790 | 172 Mpa |
| 65°C | ASTM D790 | 110 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 5960 Mpa |
| tensile strength | 断裂,80°C | ASTM D638 | 60.0 Mpa |
| 断裂,23°C | ISO 527-2 | 140 Mpa | |
| Tensile strain | 断裂,-40°C | ISO 527-2 | 3.0 % |
| Rockwell hardness | ASTM D785 | 121 | |
| Tensile modulus | 150°C | ISO 527-2 | 1860 Mpa |
| bending strength | 121°C | ASTM D790 | 76.0 Mpa |
| Tensile strain | 断裂,120°C | ISO 527-2 | 7.0 % |
| tensile strength | 断裂,150°C | ISO 527-2 | 50.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4770 Mpa |
| bending strength | -40°C | ASTM D790 | 214 Mpa |
| tensile strength | Break,121°C | ASTM D638 | 50.0 Mpa |
| Tensile strain | 断裂,80°C | ISO 527-2 | 8.0 % |
| 断裂,150°C | ISO 527-2 | 6.0 % | |
| Tensile modulus | -40°C | ISO 527-2 | 5950 Mpa |
| tensile strength | 断裂,23°C | ASTM D638 | 140 Mpa |
| bending strength | 90°C | ASTM D790 | 90.0 Mpa |
| Tensile modulus | 120°C | ISO 527-2 | 2090 Mpa |
| tensile strength | 断裂,120°C | ISO 527-2 | 50.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 121°C | ASTM D790 | 1930 Mpa |
| bending strength | 23°C | ISO 178 | 160 Mpa |
| elongation | 断裂,-40°C | ASTM D638 | 3.0 % |
| 断裂,80°C | ASTM D638 | 8.0 % | |
| Flexural modulus | 65°C | ASTM D790 | 2400 Mpa |
| 23°C | ASTM D790 | 5310 Mpa | |
| tensile strength | 断裂,-40°C | ASTM D638 | 160 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 4.0 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.60 |
| dielectric strength | IEC 60243-1 | 40 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| 1.50mm | ASTM D257 | >1.0E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| dielectric constant | 1MHz | IEC 60250 | 3.40 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020 |
| other | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| characteristic | 刚强度 高刚性 耐化学性良好 | ||
| purpose | 汽车领域应用 安全帽 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.23 |
| flammability | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 6.0mm | UL 94 | V-2 | |
| 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.50 % | |
| Water absorption rate | 饱和 | ASTM D570 | 8.1 % |
| 24hr | ASTM D570 | 1.4 % | |
| 23°C,24hr | ISO 62 | 1.4 % | |
| 平衡,50%RH | ASTM D570 | 2.3 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.3 % | |
| 饱和,23°C | ISO 62 | 8.1 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/8231G HS |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| RTI Elec | 6.0mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 200 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| RTI Str | 6.0mm | UL 746 | 105 °C |
| 0.8mm | UL 746 | 105 °C | |
| melting temperature | ASTM D3418 | 220 °C | |
| RTI Elec | 3.0mm | UL 746 | 130 °C |
| RTI Imp | 3.0mm | UL 746 | 105 °C |
| RTI Elec | 0.8mm | UL 746 | 130 °C |
| melting temperature | ISO 3146 | 220 °C | |
| RTI Imp | 0.8mm | UL 746 | 95.0 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 217 °C |
| Linear coefficient of thermal expansion | MD | 3.9E-05 cm/cm/°C | |
| RTI Str | 1.5mm | UL 746 | 105 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C |
| RTI Str | 3.0mm | UL 746 | 105 °C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 5E-05 cm/cm/°C |
| TD | 7.8E-05 cm/cm/°C | ||
| RTI Imp | 6.0mm | UL 746 | 105 °C |