Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE NG2429G DOW SPAIN
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DOW SPAIN/NG2429G |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | -20°C,1.00mm,模压成型 | ISO 6603-2 | 23.0 J |
| 23°C,滚塑成形2 | ISO 6603-2 | 17.0 J | |
| 23°C,1.00mm,模压成型 | ISO 6603-2 | 17.0 J |
| hardness | Test Condition | Test Method | DOW SPAIN/NG2429G |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ISO 868 | 57 |
| Mechanical properties | Test Condition | Test Method | DOW SPAIN/NG2429G |
|---|---|---|---|
| Tensile strain | 断裂,滚塑成形2 | ISO 527-2 | 700 % |
| tensile strength | 屈服,模压成型 | ISO 527-2 | 17.0 Mpa |
| Tensile strain | 断裂,模压成型 | ISO 527-2 | 800 % |
| tear strength | 压缩模塑 | DIN 53515 | 145 Mpa |
| tensile strength | 断裂,模压成型 | ISO 527-2 | 24.7 Mpa |
| tear strength | --3 | DIN 53515 | 140 Mpa |
| tensile strength | 屈服,滚塑成形2 | ISO 527-2 | 17.0 Mpa |
| 断裂,滚塑成形2 | ISO 527-2 | 21.8 Mpa | |
| Flexural modulus | 模压成型，1%正割 | ISO 178 | 640 Mpa |
| physical property | Test Condition | Test Method | DOW SPAIN/NG2429G |
|---|---|---|---|
| Environmental stress cracking resistance | 50°C,100%Antarox,模压成型 | ASTM D1693 | >1000 hr |
| 50°C,10%Antarox,滚塑成形2 | ASTM D1693 | 400 hr | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | DOW SPAIN/NG2429G |
|---|---|---|---|
| Crystallization peak temperature | DSC | DSC | 105 °C |
| vicat | ISO 306/A120 | 118 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 38.9 °C |
| melting temperature | DSC | 125 °C |