PC EXL1112-BR6G177 SABIC INNOVATIVE NANSHA
LEXAN™
Fitness equipment、Bottle cap、Electrical field、Electronic field
High mobility、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 69.6 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 20 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.8 % |
| tensile strength | 断裂 | ASTM D638 | 58.7 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2320 Mpa |
| Tensile modulus | ASTM D638 | 2280 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.1 Mpa |
| ISO 178 | 85.0 Mpa | ||
| Flexural modulus | ISO 178 | 2240 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 58.1 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 850 °C | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 °C |
| 1.0mm | IEC 60695-2-13 | 875 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 16.0 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 137 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| vicat | ASTM D152511 | 144 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 125 °C |
| RTI Str | UL 746 | 125 °C | |
| vicat | -- | ISO 306/B120 | 145 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/Be | 136 °C |
| vicat | -- | ISO 306/B50 | 144 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 120 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 130 °C |