Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC SLX2432T NA9D082T SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical Applications,Lighting applications,Plastic bag,Outdoor applications,Lawn garden equipment
Aging resistance,UV resistance,Antistatic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass |
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 130 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 116 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 118 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 130 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 6.7E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B120 | 137 °C |
| ASTM D152510 | 135 °C | ||
| -- | ISO 306/B50 | 135 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| Bending modulus | ISO 178 | 2500 Mpa | |
| 50.0mm跨距 | ASTM D790 | 2500 Mpa | |
| bending strength | ISO 178 | 105 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 105 Mpa | |
| elongation | 断裂 | ASTM D638 | 110 % |
| 屈服 | ASTM D638 | 6.0 % | |
| Tensile modulus | ASTM D638 | 2550 Mpa | |
| ISO 527-2/1 | 2550 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 69.0 Mpa |
| 屈服 | ASTM D638 | 67.0 Mpa | |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| 断裂 | ASTM D638 | 72.0 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| Outdoor applicability | UL 746C | f1 | |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.25 % |
| 平衡,23°C,50%RH | ISO 62 | 0.17 % | |
| 24hr | ASTM D570 | 0.12 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 30 kJ/m² |
| -30°C | ISO 179/1eA | 15 kJ/m² | |
| Dart impact | -40°C,TotalEnergy | ASTM D3763 | 85.0 J |
| 23°C,TotalEnergy | ASTM D3763 | 77.0 J | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| 23°C | ISO 180/1A | 25 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| Extreme Oxygen Index | ISO 4589-2 | 38 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/SLX2432T NA9D082T |
|---|---|---|---|
| Refractive index | ASTM D542 | 1.590 | |
| transmissivity | 2540µm | ASTM D1003 | 84.0 % |
| turbidity | 2540µm | ASTM D1003 | 0.80 % |