PC 9330-759 SABIC INNOVATIVE NANSHA
LEXAN™ 
--
Flame retardant,Toughening,UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°C9ISO 180/1U无断裂
Dart impact23°C,TotalEnergyASTM D376352.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°C11内部方法1100 J/m
23°C9ISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
ball-indentation hardnessH358/30ISO 2039-190.0 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
bending strength屈服,50.0mm跨距5ASTM D79088.0 Mpa
tensile strength 屈服4ASTM D63858.0 Mpa
elongation断裂4ASTM D638130 %
Tensile modulus--3ASTM D6382100 Mpa
elongation断裂ISO 527-2/50130 %
Flexural modulus50.0mm跨距5ASTM D7902070 Mpa
bending strength--6,7ISO 17885.0 Mpa
Flexural modulus--6ISO 1782200 Mpa
tensile strength 断裂ISO 527-2/5060.0 Mpa
屈服ISO 527-2/5055.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服4ASTM D6386.0 %
tensile strength 断裂4ASTM D63861.0 Mpa
Tensile modulus--ISO 527-2/12100 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
Dissipation Factor50HzASTM D1502.4E-03
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
Dissipation Factor60HzASTM D1502.4E-03
High arc combustion index (HAI)HAIUL 746PLC 0
Dissipation Factor1MHzASTMD1508.5E-03
dielectric strength3.20mm,在油中IEC 60243-116 KV/mm
Dissipation Factor50HzIEC 602501E-03
60HzIEC 602501E-03
dielectric strength3.20mm,inOilASTM D14917 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Hot wire ignition (HWI)HWIUL 746PLC 1
Surface ResistivityIEC 60093>1.0E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
UL flame retardant rating3.0mmUL 945VA
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating0.8mmUL 94V-1
1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-235 %
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
Shrinkage rateMD:3.20mm内部方法0.40-0.80 %
Outdoor applicabilityUL 746Cf1
Melt volume flow rate300°C/1.2kgISO 11339.00 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.15 %
饱和,23°CISO 620.35 %
Shrinkage rateTD:3.20mm内部方法0.40-0.80 %
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/9330-759
Linear coefficient of thermal expansionTD:23到80°CISO 11359-27.7E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D648124 °C
Linear coefficient of thermal expansionMD:23到80°CISO 11359-27.2E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648134 °C
RTIUL 746120 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8316.7E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,100mm跨距12，HDTISO 75-2/Ae124 °C
Linear coefficient of thermal expansionTD:-40到40°CASTME8316.7E-05 cm/cm/°C
vicat--ISO 306/B50140 °C
RTI ImpUL 746115 °C
Heat distortion temperature0.45MPa,未退火,100mm跨距12，HDTISO 75-2/Be135 °C
1.8MPa,未退火,3.20mm，HDTASTM D648120 °C
vicat--ASTMD152513142 °C
RTI ElecUL 746125 °C
ball-indentation hardness125°CIEC 60695-10-2通过