PPS C-140SC IDEMITSU JAPAN
--
plastic pallet、Automotive Applications
High mobility、High temperature resistan、Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 103 M（Scale） |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 280 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| elongation at break | 23°C | ISO 527-2 | 2 % |
| tensile strength | 23°C | ISO 527-2 | 184 Mpa |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| dielectric constant | IEC 60250 | 3.90 | |
| dielectric strength | 3.00mm | IEC 60243-1 | 13 KV/mm |
| Flame retardant performance | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 0.75mm |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | >0.020 % |
| Shrinkage rate | TD | ISO 294-4 | 0.40 % |
| MD | ISO 294-4 | 0.70 % | |
| density | ISO 1183 | 1.65 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/C-140SC |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 272 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5E-05 cm/cm/°C |