Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS XP-2140C NP Samsung Cheil South Korea
INFINO®
Automotive Applications、Laptop case、Application in the automo
enhance、Flame retardant、Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 85 J/m |
| 23°C | ISO 180/1A | 11 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 98 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 121 |
| R级 | ASTM D785 | 121 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 180 Mpa |
| Tensile modulus | ASTM D638 | 6860 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 180 Mpa |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ISO 178 | 260 Mpa | |
| Flexural modulus | ISO 178 | 13400 Mpa | |
| bending strength | ASTM D790 | 265 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.7 % |
| Tensile modulus | ISO 527-2/5 | 11400 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 177 Mpa |
| 屈服 | ASTM D638 | 186 Mpa | |
| Flexural modulus | ASTM D790 | 12700 Mpa |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| ash content | ASTM D5630 | 40 % | |
| melt mass-flow rate | 316°C/5.0kg | ASTM D1238 | 55 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.27-0.33 % |
| TD：3.20mm | ASTM D955 | 0.32-0.39 % | |
| density | ASTM D792 | 1.66 g/cm³ | |
| ISO 1183 | 1.66 g/cm³ | ||
| melt mass-flow rate | 316°C/5.0kg | ISO 1133 | 83 g/10min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/XP-2140C NP |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 267 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 270 °C | |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 283 °C | |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 272 °C | |
| 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 282 °C | |
| 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 283 °C |