PA66 A3WG10 BASF GERMANY
Ultramid®
Industrial applications
Oil resistant,Dimensional stability,High rigidity,heat-resisting,Filler: Glass fiber reinf,50% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3WG10 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 15 kJ/m² |
| -30°C | ISO 179 | 13 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 17 kJ/m² |
| -40°C | ISO 180 | 14 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 85 kJ/m² |
| 23°C | ISO 179 | 95 kJ/m² |
| thermal performance | Test Condition | Test Method | BASF GERMANY/A3WG10 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 262 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 256 °C | |
| melting temperature | ISO 3146 | 260 °C |
| mechanical properties | Test Condition | Test Method | BASF GERMANY/A3WG10 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 360 Mpa |
| flexural modulus | 23°C | ISO 178 | 15300 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 17000 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| tensile strength | 断裂,23°C | ISO 527-2 | 240 Mpa |
| Physical properties | Test Condition | Test Method | BASF GERMANY/A3WG10 |
|---|---|---|---|
| density | ISO 1183 | 1.57 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 4.0 % |
| 平衡,23°C,50%RH | ISO 62 | 1.2 % |