PA66 HTNFR51G35L BK337 DUPONT SHENZHEN

Zytel®

Electrical appliances,Automotive interior equipment,Household appliances

Aging resistance,High temperature resistan,Glass fiber reinforced,enhance,Flame retardant

Plastic Datasheets

hardness	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Rockwell hardness	M-Sale	ISO 2039-2	108
Rockwell hardness		R-Sale	ISO 2039-2	124

Supplementary Information	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Odor		VDA270	4.00

thermal performance	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	284 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	260 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.5E-05 cm/cm/°C
		MD：--	ISO 11359-2	1.8E-05 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	1.8E-05 cm/cm/°C
		TD：--	ISO 11359-2	5.5E-05 cm/cm/°C
Melting temperature		ISO 11357-3	300 °C

mechanical properties	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Bending modulus		ISO 178	10300 Mpa
bending strength		ISO 178	300 Mpa
Poisson's ratio		ISO 527	0.39
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile creep modulus		1000hr	ISO 899-1	-- Mpa
Tensile modulus		ISO 527-2	12000 Mpa
Tensile strain	Break	ISO 527-2	2.4 %
tensile strength	Break	ISO 527-2	210 Mpa

Electrical performance	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Compared to the anti leakage trace index		IEC 60112	V
Dielectric strength		IEC 60243-1	36 KV/mm
Relative permittivity	100Hz	IEC 60250	4.00
Relative permittivity		1MHz	IEC 60250	4.00
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Shrinkage rate	MD	ISO 294-4	0.20 %
Shrinkage rate		TD	ISO 294-4	0.60 %
SpecificHeatCapacity of Melt			1860 J/kg/°C
ThermalConductivityofMelt			0.25 W/m/K
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	4.5 %

impact performance	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	70 kJ/m²

flammability	Test Condition	Test Method	DUPONT SHENZHEN/HTNFR51G35L BK337
Burning rate	1.00mm	ISO 3795	23 mm/min
Extreme Oxygen Index		ISO 4589-2	24 %
FMVSS flammability		FMVSS302	B
UL flame retardant rating	0.9mm	IEC 60695-11-10,-20	HB
		1.5mm	IEC 60695-11-10,-20	HB
		1.5mm	UL 94	HB
		0.9mm	UL 94	HB