PC
PC SABIC INNOVATIVE NANSHA CFR7431 NA8E061TNS
Flame retardant grade
US$ 7,010 / MT
FOB Guangzhou port, China
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
Dissipation factor1.10GHzASTMES7-835.7E-03
Dielectric constant1.10GHzASTMES7-832.79
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
elongationBreakASTM D63855 %
bending strengthISO 178101 Mpa
Tensile modulusASTM D6382520 Mpa
bending strengthYield,50.0mmSpanASTM D790107 Mpa
tensile strengthBreakASTM D63855.0 Mpa
Bending modulusISO 1782450 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
Bending modulus50.0mmSpanASTM D7902450 Mpa
Tensile modulusISO 527-2/12350 Mpa
tensile strengthBreakISO 527-2/5053.0 Mpa
YieldISO 527-2/5066.0 Mpa
Tensile strainBreakISO 527-2/5056 %
tensile strengthYieldASTM D63867.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
Linear coefficient of thermal expansionTD：-40to40°CASTME8316.7E-05 cm/cm/°C
MD：23to80°CISO 11359-27.7E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.9E-05 cm/cm/°C
RTI StrUL 746125 °C
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be131 °C
1.8MPa,Unannealed,100mmSpanISO 75-2/Ae120 °C
Vicat softening temperatureASTM D152510136 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648120 °C
Vicat softening temperature--ISO 306/B50137 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8316.7E-05 cm/cm/°C
RTI ElecUL 746125 °C
RTI ImpUL 746120 °C
Vicat softening temperature--ISO 306/B120139 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648131 °C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Shrinkage rateTD：3.20mmInternal Method0.60-0.80 %
Outdoor applicabilityUL 746Cf1
Water absorption rateEquilibrium,23°C,50%RHISO 620.10 %
Shrinkage rateMD：3.20mmInternal Method0.55-0.75 %
Water absorption rateSaturation,23°CISO 620.13 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Charpy Notched Impact Strength-30°CISO 179/1eA7.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Dart impact23°C,TotalEnergyASTM D376364.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A8.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
UL flame retardant rating0.40mmUL 94V-2
Hot filament ignition temperature1.2mmIEC 60695-2-13850 °C
UL flame retardant rating3.0mmUL 945VA
1.0mmUL 94V-1
1.2mmUL 94V-0
Burning wire flammability index1.2mmIEC 60695-2-12960 °C
optical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/CFR7431 NA8E061TNS
transmissivity1000μmInternal Method>90.0 %
3000μmInternal Method>88.0 %
2000μmInternal Method>89.0 %

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China