Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM F30-73R1 MITSUBISHI ENGINEERING JAPAN
Iupital™
Electronic and Electrical、Automotive sector
Weather resistance、Medium viscosity、Low viscosity、Mold deposition improveme
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-73R1 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.2mm | ASTM D256 | 54 J/m |
| Rockwell hardness | ASTM D785 | 80 M | |
| tensile strength | 23℃ | ASTM D638 | 62.3 Mpa |
| bending strength | 23℃ | ASTM D790 | 91.2 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 2.62 GPa |
| Stretching length | 23℃ | ASTM D638 | 50 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-73R1 |
|---|---|---|---|
| Dielectric loss | 10，正切 | ASTM D150 | 0.007 |
| Surface Resistivity | ASTM D257 | 1×10 | |
| dielectric strength | ASTM D149 | 19 MV/m | |
| dielectric constant | 10 | ASTM D150 | 33 Pf/m |
| Volume resistivity | ASTM D257 | 1×10 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-73R1 |
|---|---|---|---|
| Shrinkage rate | 平行方向 | 2.0 % | |
| melt mass-flow rate | ASTM D1238 | 27 g/10min | |
| Water absorption rate | ASTM D570 | 0.22 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-73R1 |
|---|---|---|---|
| Heat distortion temperature | 455Kpa，HDT | ASTM D648 | 158 °C |
| 820Kpa，HDT | ASTM D648 | 110 °C | |
| UL flame retardant rating | UL 94 | HB |