PA/MXD6 1002F BK MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and Electrical、Automotive sector
High rigidity、High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1002F BK |
|---|---|---|---|
| Filling amount | 30 % |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1002F BK |
|---|---|---|---|
| Stretching length | ASTM D638 | 2.0 % | |
| Flexural modulus | ASTM D790 | 11.6/9.8 GPa | |
| Rockwell hardness | ASTM D785 | 112 M | |
| Impact strength of cantilever beam gap | ASTM D256 | 82/76 J/m | |
| compressive strength | ASTM D695 | 240 Mpa | |
| tensile strength | ASTM D638 | 202/158 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1002F BK |
|---|---|---|---|
| dielectric strength | ASTM D149 | 30.4 MV/m | |
| Dielectric loss | 正切 | ASTM D150 | 0.010 |
| dielectric constant | ASTM D150 | 32 Pf/m |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1002F BK |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.51 % | |
| Water absorption rate | 23℃,24H | ASTM D570 | 0.2 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1002F BK |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648 | 232 °C |
| UL flame retardant rating | UL 94 | HB |