HDPE M200056 SABIC SAUDI
SABIC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC SAUDI/M200056 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,模压成型 | ISO 180/A | 3.0 kJ/m² |
| hardness | Test Condition | Test Method | SABIC SAUDI/M200056 |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ISO 868 | 62 |
| Mechanical properties | Test Condition | Test Method | SABIC SAUDI/M200056 |
|---|---|---|---|
| bending strength | 2.00mm,模压成型 | ISO 178 | 28.0 Mpa |
| Tensile modulus | 2.00mm,模压成型 | ISO 527-2/1BA/50 | 1200 Mpa |
| elongation | 断裂,2.00mm,模压成型 | ASTM D638 | >200 % |
| tensile strength | 断裂,2.00mm,模压成型 | ASTM D638 | 15.0 Mpa |
| Flexural modulus | 2.00mm,模压成型 | ISO 178 | 1350 Mpa |
| tensile strength | 屈服,2.00mm,模压成型 | ASTM D638 | 28.0 Mpa |
| physical property | Test Condition | Test Method | SABIC SAUDI/M200056 |
|---|---|---|---|
| Environmental stress cracking resistance | 60°C,3.00mm,Rhodacal-DS10,模压成型 | 内部方法 | 60.0 hr |
| density | ISO 1183 | 0.956 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/M200056 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 132 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 85.0 °C |
| vicat | ISO 306/A | 128 °C | |
| EnthalpyChange | ISO 11357-3 | 210 J/g |