PC EHR3150 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Casters,Electronic field,Electrical field
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EHR3150 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 6.0E+15 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 3.0E+16 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EHR3150 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 89.0 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2600 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2700 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 13 % | |
| tensile strength | ASTM D638/ISO 527 | 54.0 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EHR3150 |
|---|---|---|---|
| characteristic | High Reflectivty、磷含量.低（-无）、无溴 | ||
| notes | 以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EHR3150 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40-0.60 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EHR3150 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 134 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000063 mm/mm.℃ |