PA6 BKV50H3.0 000000 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 95 kJ/m² |
| 23°C | ISO 180/1U | 95 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 90 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GHR.14-160.GF50 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 23°C | ISO 178/A | 15500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 225 Mpa |
| bending strength | 23°C | ISO 178 | 360 Mpa |
| Bending Strain | 23°C | 3.0 % | |
| Tensile modulus | 23°C | ISO 527-2/1 | 16800 Mpa |
| flammability | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| Burning Behavior | >1.00mm | ISO 3795 | passed |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| Shrinkage rate | MD:280°C,3.00mm2 | ISO 2577 | 0.16 % |
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.5 % |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO 2577 | 0.85 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.0 % |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO 2577 | 0.020 % |
| TD:120°C,2hr,3.00mm3 | ISO 294-4 | 0.050 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/BKV50H3.0 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 222 °C | |
| vicat | -- | ISO 306/B120 | >200 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| vicat | -- | ISO 306/B50 | >200 °C |