PC AC3610 FCFC TAIWAN
TAIRILITE®
Automotive sector
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3610 |
---|---|---|---|
Hot deformation temperature | 热变形温度,1.8MPa,未退水,3.18mmSpan | ISO 75-2/A | 121 °C |
1.8MPa,未退水,3.18mm | ASTM D-648 | 121 °C |
flame retardant performance | Test Condition | Test Method | FCFC TAIWAN/AC3610 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3610 |
---|---|---|---|
Bending modulus | 23℃ | ASTM D-790(ISO 178) | 2060 Mpa |
bending strength | 23℃ | ASTM D-790(ISO 178) | 100 Mpa |
Izod Unnotched Impact Strength | 23℃,3.18mm | ASTM D-256 | 740 J/m |
Rockwell hardness | 23℃ | ASTM D-785(ISO 2039/2) | 121 |
tensile strength | Yield,23℃ | ASTM D-638(ISO 527-2) | 59 Mpa |
Physical properties | Test Condition | Test Method | FCFC TAIWAN/AC3610 |
---|---|---|---|
density | 23℃,比重 | ASTM D-792(ISO 1183) | 1.19 g/cm³ |
melt mass-flow rate | 300℃,1.2kg | ASTM D-1238(ISO 1133) | 10 g/10min |
Shrinkage rate | 23℃ | Internal Method | 0.5-0.7 % |