Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS Generic PPS - GlassMineral Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodGeneric/Generic PPS - GlassMineral
Charpy Notched Impact Strength23°CISO 1793.9to9.1 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25638to100 J/m
Suspended wall beam without notch impact strength23°CISO 18020 kJ/m²
Impact strength of cantilever beam gap23°CISO 1805.9to7.0 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D256200to320 J/m
Impact strength of simply supported beam without notch23°CISO 1795.3to31 kJ/m²
hardnessTest ConditionTest MethodGeneric/Generic PPS - GlassMineral
Rockwell hardness23°CISO 2039-297to124
23°CASTM D78599to122
Mechanical propertiesTest ConditionTest MethodGeneric/Generic PPS - GlassMineral
tensile strength 断裂,23°CASTM D638110to165 MPa
bending strength23°CASTM D790172to261 MPa
Tensile modulus23°CISO 527-210600to23000 MPa
tensile strength 屈服,23°CISO 527-2129to173 MPa
compressive strength23°CASTM D695138to295 MPa
Taber abraser23°CASTM D104470.0to70.8 mg
shear strength23°CASTM D73260.0to65.6 MPa
elongation断裂,23°CISO 527-20.43to1.8 %
Flexural modulus23°CISO 17810700to22100 MPa
tensile strength 23°CASTM D638100to174 MPa
coefficient of frictionASTM D18940.30to0.35
Tensile modulus23°CASTM D63814200to19100 MPa
tensile strength 断裂,23°CISO 527-250.0to167 MPa
Flexural modulus23°CASTM D79012800to20100 MPa
tensile strength 23°CISO 527-2113to172 MPa
Poisson's ratio23°CASTME1320.34to0.36
elongation断裂,23°CASTM D6380.50to2.1 %
bending strength23°CISO 178126to262 MPa
Electrical performanceTest ConditionTest MethodGeneric/Generic PPS - GlassMineral
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
dielectric constant23°CIEC 602505.15
Surface ResistivityASTM D2573.0E+3到1.0E+16 ohms
Volume resistivity23°CASTM D2575.5E+2到2.5E+16 ohms·cm
dielectric strength23°CIEC 60243-113to26 kV/mm
Dissipation Factor23°CASTM D1508.0E-4到9.2E-3
23°CIEC 602501.0E-3到2.1E-3
Volume resistivity23°CIEC 600931.0E+2到1.3E+16 ohms·cm
dielectric strength23°CASTM D14911to18 kV/mm
dielectric constant23°CASTM D1503.78to5.04
arc resistanceASTM D495180to186 sec
physical property Test ConditionTest MethodGeneric/Generic PPS - GlassMineral
Shrinkage rate23°CISO 294-40.14to0.70 %
density23°CISO 11831.81to2.00 g/cm³
Shrinkage rateMD:23°CASTM D9550.15to0.31 %
Water absorption rate23°C,24hrISO 620.019to0.020 %
density--ASTM D7921.79to2.00 g/cm³
Shrinkage rateTD:23°CASTM D9550.38to1.0 %
Water absorption rate23°C,24hrASTM D5700.020to0.025 %
饱和,23°CISO 620.020 %
Thermal performanceTest ConditionTest MethodGeneric/Generic PPS - GlassMineral
Linear coefficient of thermal expansionTDASTM D6961.7E-5到4.8E-5 cm/cm/°C
melting temperatureISO 11357-3278to280 °C
Heat distortion temperature1.8MPa,未退火，HDTASTM D648259to270 °C
Linear coefficient of thermal expansionTDASTME8313.0E-5到7.0E-5 cm/cm/°C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A259to276 °C
Linear coefficient of thermal expansionMDASTM D6964.0E-6到2.0E-5 cm/cm/°C
MDISO 11359-29.6E-6到2.4E-5 cm/cm/°C
Heat distortion temperature8.0MPa,未退火，HDTISO 75-2/C215to220 °C
Linear coefficient of thermal expansionMDASTME8311.0E-5到1.5E-5 cm/cm/°C
TDISO 11359-21.9E-5到3.3E-5 cm/cm/°C