Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP X M3 T15 LYONDELLBASELL HOLAND
Hifax
Car dashboard、Automotive interior parts、Automotive sector、Application in the automo
scratch resistance 、Moderate liquidity、UV resistance、Mineral reinforcement、enhance、Filler: Mineral filler、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M3 T15 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| -30°C | ISO 179/1eU | 25 kJ/m² |
| hardness | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M3 T15 |
|---|---|---|---|
| Shore hardness | 邵氏D,3秒 | ISO 868 | 62 |
| 邵氏D,15秒 | ISO 868 | 60 |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M3 T15 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 21.0 Mpa |
| Flexural modulus | 正割 | ISO 178 | 2500 Mpa |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M3 T15 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 1.0-1.4 % | |
| Melt volume flow rate | 230°C/5.0kg | ISO 1133 | 30.0 cm3/10min |
| 230°C/2.16kg | ISO 1133 | 7.00 cm3/10min | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/X M3 T15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 100 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 55.0 °C |