PBT 1100M TORAY JAPAN
Toraycon® 
Electrical field、Electronic field、Casters、PBT board、Bottle cap、Profile、Household appliances、Household appliances、Fitness equipment
wear resistant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodTORAY JAPAN/1100M
Impact strength of cantilever beam gapASTM D256/ISO 1794.4 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 17887 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D790/ISO 1782.5 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D79084.0 Mpa
elongationASTM D638/ISO 52732 %
elongation at breakASTM D638/ISO 52732 %
Flexural modulusASTM D7902500 Mpa
bending strengthISO 17887 MPa
tensile strength ISO 527-260.0 Mpa
elongation断裂ASTM D63827 %
Flexural modulusISO 1782.5 Gpa
bending strengthISO 17887.0 Mpa
Tensile strain断裂ISO 527-232 %
Flexural modulusISO 1782500 Mpa
tensile strength 屈服ASTM D63857.0 Mpa
otherTest ConditionTest MethodTORAY JAPAN/1100M
characteristic注塑
Physical propertiesTest ConditionTest MethodTORAY JAPAN/1100M
densityASTM D792/ISO 11831.315
melt mass-flow rateASTM D1238/ISO 113359 g/10min
physical property Test ConditionTest MethodTORAY JAPAN/1100M
Viscosity value0.5%OCP内部方法85.0 cm³/g
Melt volume flow rateISO 113359 cm
melt mass-flow rate250°C/1.0kgISO 113331 g/10min
Melt volume flow rate250°C/2.16kgISO 113359.0 cm3/10min
Thermal performanceTest ConditionTest MethodTORAY JAPAN/1100M
melting temperature224 °C
224 ℃（℉）
UL flame retardant ratingUL94HB