Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 D3G7 BK 20560 BASF SHANGHAI
Ultramid®
Gear bearing、Automotive components、Air transportation indust
High rigidity、Heat aging、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/D3G7 BK 20560 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 60 kJ/m² |
| 23°C | ISO 179 | 80 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/D3G7 BK 20560 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.9 % |
| bending strength | 23°C | ISO 178 | 300 Mpa |
| tensile strength | 断裂,150°C | ISO 527-2 | 84.0 Mpa |
| Tensile strain | 断裂,150°C | ISO 527-2 | 6.7 % |
| Flexural modulus | 23°C | ISO 178 | 10600 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 11300 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 200 Mpa |
| Tensile modulus | 150°C | ISO 527-2 | 4200 Mpa |
| Electrical performance | Test Condition | Test Method | BASF SHANGHAI/D3G7 BK 20560 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 48 KV/mm | |
| Volume resistivity | IEC 60093 | 3E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| physical property | Test Condition | Test Method | BASF SHANGHAI/D3G7 BK 20560 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.87 % |
| MD | ISO 294-4 | 0.30 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/D3G7 BK 20560 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| Linear coefficient of thermal expansion | MD | 1.4E-5to2.0E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 240 °C |
| Linear coefficient of thermal expansion | TD | 8.0E-5to1.3E-4 cm/cm/°C | |
| melting temperature | ISO 3146 | 260 °C |