PA6 K223-TP4 DSM HOLAND
Akulon®
--
High impact resistance、High toughness、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 18 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | > 50 % | |
| bending strength | ISO 178 | 65.0 Mpa | |
| Flexural modulus | ISO 178 | 1600 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.0 % |
| tensile strength | 屈服 | ISO 527-2 | 50.0 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.016 |
| dielectric strength | IEC 60243-1 | 27 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Dissipation Factor | 100 Hz | IEC 60250 | 3.0E-3 |
| relative permittivity | 1 MHz | IEC 60250 | 2.70 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 725 °C |
| 2.0 mm | IEC 60695-2-13 | 725 °C | |
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 700 °C |
| Flammability level | UL 94 | HB | |
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.3 % |
| density | ISO 1183 | 1.07 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 1.4 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 8.5 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.7 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/K223-TP4 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 130 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 55.0 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.2E-4 cm/cm/°C |