PCTG EX401 EASTMAN USA
Tritan™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C2 | 内部方法 | 650 J/m |
Dart impact | 23°C,EnergyatMaxLoad | ASTM D3763 | 59.0 J |
Impact strength of cantilever beam gap | -40°C | ASTM D256 | 130 J/m |
23°C3 | 内部方法 | 640 J/m | |
23°C | ASTM D256 | 650 J/m | |
23°C | ISO 180 | 66 kJ/m² | |
Dart impact | -40°C,EnergyatMaxLoad | ASTM D3763 | 63.0 J |
Impact strength of cantilever beam gap | 23°C | ASTM D4812 | NoBreak |
-40°C | ASTM D4812 | NoBreak | |
-40°C | ISO 180 | 14 kJ/m² |
hardness | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
Rockwell hardness | R计秤,23°C | ASTM D785 | 115 |
Supplementary Information | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
MicrowaveBoiling-OvenPower | 内部方法 | <2200 Watts | |
Shrinkage rate | Boiling,1hr | 内部方法 | <1.0 % |
Boiling,2hr | 内部方法 | <1.5 % | |
ThermalShock-WaterImmersion | 35to98°C | 内部方法 | Noeffect |
MicrowaveSteamSterilization-TotalEnergy | 内部方法 | <11200 W-min | |
Shrinkage rate | Dishwasher | 内部方法 | <1.0 % |
Mechanical properties | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
Tensile modulus | 23°C | ASTM D638 | 1590 Mpa |
23°C | ISO 527-2 | 1620 Mpa | |
tensile strength | 屈服,23°C2 | 内部方法 | 44.0 Mpa |
断裂,23°C | ISO 527-2 | 49.0 Mpa | |
屈服,23°C | ASTM D638 | 44.0 Mpa | |
断裂,23°C | ASTM D638 | 53.0 Mpa | |
Tensile strain | 断裂,23°C | ISO 527-2 | 130 % |
tensile strength | 屈服,23°C3 | 内部方法 | 45.0 Mpa |
屈服,23°C | ISO 527-2 | 45.0 Mpa | |
Tensile strain | 屈服,23°C | ISO 527-2 | 7.0 % |
Flexural modulus | 23°C | ISO 178 | 1530 Mpa |
elongation | 屈服,23°C | ASTM D638 | 7.0 % |
bending strength | 屈服,23°C | ASTM D790 | 66.0 Mpa |
elongation | 屈服,23°C3 | 内部方法 | 6.5 % |
Flexural modulus | 23°C | ASTM D790 | 1590 Mpa |
elongation | 屈服,23°C2 | 内部方法 | 7.0 % |
断裂,23°C | ASTM D638 | 140 % |
optical performance | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
transmissivity | 总计 | ASTM D1003 | 92.0 % |
Haze ratio | --2 | 内部方法 | <1.0 % |
-- | ASTM D1003 | <1.0 % |
physical property | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
Shrinkage rate | MD:BlowMolded | 内部方法 | 1.2-1.6 % |
density | ASTM D792 | 1.17 g/cm³ | |
Shrinkage rate | MD:注塑 | ASTM D955 | 0.50-0.70 % |
Thermal performance | Test Condition | Test Method | EASTMAN USA/EX401 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 92.0 °C |
0.45MPa,未退火,HDT | ASTM D648 | 109 °C |