Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PETG 0601 EASTMAN USA
--
sporting goods、chip
High transparency、High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C,3.20mm | ASTM D4812 | 无断裂 |
| Dart impact | -40°C,2.50mm,EnergyatPeakLoad | ASTM D3763 | 41.0 J |
| 23°C,3.20mm,EnergyatPeakLoad | ASTM D3763 | 33.0 J | |
| Suspended wall beam without notch impact strength | -20°C,3.20mm | ASTM D4812 | 无断裂 |
| -30°C7 | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C,3.20mm,能量到力量峰值8,9 | ISO 6603-2 | 44.0 J |
| -40°C,2.50mm,能量到力量峰值8,9 | ISO 6603-2 | 35.0 J | |
| Suspended wall beam without notch impact strength | 23°C7 | ISO 180/1U | 无断裂 |
| 23°C,3.20mm | ASTM D4812 | 无断裂 | |
| Dart impact | 23°C,2.50mm,能量到力量峰值8,9 | ISO 6603-2 | 40.0 J |
| -40°C,3.20mm,能量到力量峰值8,9 | ISO 6603-2 | 36.0 J | |
| -40°C,3.20mm,EnergyatPeakLoad | ASTM D3763 | 50.0 J | |
| Suspended wall beam without notch impact strength | -20°C7 | ISO 180/1U | 无断裂 |
| Dart impact | 23°C,2.50mm,EnergyatPeakLoad | ASTM D3763 | 28.0 J |
| Suspended wall beam without notch impact strength | -40°C,3.20mm | ASTM D4812 | 无断裂 |
| -40°C7 | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 106 |
| R计秤,23°C | ISO 2039-2 | 109 |
| film | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| tear strength | M.D.:23°C | ASTM D1938 | 36 kN/m |
| elongation | MD:断裂 | ASTM D882 | 400 % |
| tensile strength | MD:屈服 | ASTM D882 | 52.0 Mpa |
| Water Vapor Transmission Rate | 38°C,100%RH | ASTMF1249 | 7.0 g/m²/24hr |
| Secant modulus | MD | ASTM D882 | 1900 Mpa |
| Dart impact | -18°C | ASTM D1709A | 500 g |
| elongation | TD:屈服 | ASTM D882 | 4.0 % |
| tensile strength | TD:屈服 | ASTM D882 | 52.0 Mpa |
| Elmendorf tear strength | MD | ASTM D1922 | 1400 g |
| OTr | 23°C | ASTM D3985 | 10 cm³·mm/m²/atm/24hr |
| Secant modulus | TD | ASTM D882 | 1900 Mpa |
| Carbon dioxide transmittance | 23°C | ASTM D1434 | 49 cm³·mm/m²/atm/24hr |
| film thickness | 250 µm | ||
| tensile strength | MD:断裂 | ASTM D882 | 59.0 Mpa |
| tear strength | T.D.:23°C | ASTM D1938 | 36 kN/m |
| tensile strength | TD:断裂 | ASTM D882 | 55.0 Mpa |
| elongation | MD:屈服 | ASTM D882 | 4.0 % |
| Tear resistance of pants | TD | ISO 6383-1 | 36.0 N/mm |
| Elmendorf tear strength | TD | ASTM D1922 | 1700 g |
| Dart impact | 23°C | ASTM D1709A | 400 g |
| Tear resistance of pants | MD | ISO 6383-1 | 36.0 N/mm |
| elongation | TD:断裂 | ASTM D882 | 400 % |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| elongation | 断裂,23°C | ISO 527-2 | 100 % |
| Tensile modulus | 23°C | ASTMD638 | 2100 Mpa |
| tear strength | T.D.:23°C | - | 93 N |
| bending strength | 23°C | ISO 178 | 68.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2000 Mpa |
| tear strength | M.D.:23°C | - | 93 N |
| tensile strength | 断裂,23°C | ASTMD638 | 28.0 Mpa |
| bending strength | 屈服,23°C | ASTM D790 | 70.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2100 Mpa |
| tensile strength | 屈服,23°C | ASTMD638 | 50.0 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 130 % |
| Electrical performance | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| dielectric constant | 23°C,1kHz | ASTM D150 | 2.60 |
| 23°C,1MHz | ASTM D150 | 2.40 | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Dissipation Factor | 23°C,1kHz | ASTM D150 | 5E-03 |
| Volume resistivity | 23°C | ASTM D257 | 1E+15 ohms·cm |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 0.020 |
| dielectric strength | 23°C | ASTM D149 | 16 KV/mm |
| arc resistance | ASTM D495 | 158 sec |
| optical performance | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| transmissivity | 总计 | ASTM D1003 | 91.0 % |
| gloss | 45° | ASTM D2457 | 108 |
| Haze ratio | ASTM D1003 | 0.80 % | |
| transmissivity | 常规 | ASTM D1003 | 89.0 % |
| transparency | ASTM D1746 | 85.0 |
| physical property | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| intrinsic viscosity | Film:23°C | 内部方法 | 0.70 |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.13 % |
| intrinsic viscosity | Pellets:23°C | 内部方法 | 0.75 |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/0601 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 64.0 °C |
| vicat | ASTM D1525 | 85.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到40°C | ASTM D696 | 5.1E-05 cm/cm/°C |
| specific heat | 60°C | DSC | 1300 J/kg/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 70.0 °C |
| Glass Transition Temperature | DSC | 80.0 °C | |
| specific heat | 150°C | DSC | 1880 J/kg/°C |
| 200°C | DSC | 1970 J/kg/°C | |
| thermal conductivity | 23°C | ASTMC177 | 0.21 W/m/K |
| specific heat | 100°C | DSC | 1760 J/kg/°C |
| 250°C | DSC | 2050 J/kg/°C |