PC+PET POCAN® C 1206 000000 LANXESS GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/POCAN® C 1206 000000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 55 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 50 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Supplementary Information | Test Condition | Test Method | LANXESS GERMANY/POCAN® C 1206 000000 |
|---|---|---|---|
| ISO Shortcut | ISO 7792 | PET+PC,GHMPR,09-020 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/POCAN® C 1206 000000 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 50.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 4.5 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 10 % |
| bending strength | 3.5%Strain | ISO 178/A | 65.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2200 MPa |
| Flexural modulus | 23°C | ISO 178/A | 2200 MPa |
| bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 5.0 % | |
| 23°C | ISO 178 | 75.0 MPa |
| physical property | Test Condition | Test Method | LANXESS GERMANY/POCAN® C 1206 000000 |
|---|---|---|---|
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.30 % |
| density | 23°C | ISO 1183 | 1.22 g/cm³ |
| Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.70 % |
| Apparent density | ISO 60 | 0.80 g/cm³ | |
| Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.70 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.30 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/POCAN® C 1206 000000 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 250 °C | |
| vicat | ISO 306/B120 | 130 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 120 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |