Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E471iVF2201 CELANESE USA
--
Laptop case,Electronic and Electrical Applications,SMT application,Communication equipment,Card slot
Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 60 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| hardness | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 55 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 13800 Mpa | |
| bending strength | 23°C | ISO 178 | 180 Mpa |
| Compression Modulus | ISO 604 | 11000 Mpa | |
| Compressive Stress | 1%Strain | ISO 604 | 82.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 13500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 130 Mpa |
| Fracture bending strain | ISO 178 | 2.5 % | |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| Electrical performance | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 53 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.031 |
| flammability | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.50 % |
| MD | ISO 294-4 | 0.10 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2E-03 % |
| 饱和,23°C | ISO 62 | 0.015 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/E471iVF2201 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 335 °C | |
| vicat | ISO 306/B50 | 200 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 265 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6E-06 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 220 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.8E-05 cm/cm/°C |